Design of oxygen-doped TiZrHfNbTa refractory high entropy alloys with enhanced strength and ductility

L. K. Iroc, O. U. Tukac, B. B. Tanrisevdi, Osman El-Atwani, Matheus Tunes, Y. E. Kalay, E. Aydogan

Publikation: Beitrag in FachzeitschriftArtikelForschungBegutachtung

3 Zitate (Scopus)

Abstract

Refractory high entropy alloys (RHEAs) are considered promising materials for high-temperature applications due to their thermal stability and high-temperature mechanical properties. However, most RHEAs have high density (>10 g/cm3) and exhibit limited ductility at low temperatures and softening at high temperatures. In this study, we show that oxygen-doping can be used as a new alloy design strategy for tailoring the mechanical behavior of the TiZrHfNbTa alloy: a novel low-density (7.98 g/cm3) ductile RHEA. Even though the material is a single-phase BCC with some oxides at room temperature, secondary BCC and HCP nano-lamellar structures start to form above 600 °C in addition to the nano-twins which are shown to be stable up to 1000 °C. This alloy shows superior strength and compressive ductility due to the nanoengineered microstructure. The present study sheds light on tailoring the strength-ductility balance in RHEAs by controlling the microstructure of novel RHEAs at the nanoscale via oxygen-doping.
OriginalspracheEnglisch
Aufsatznummer111239
Seitenumfang12
FachzeitschriftMaterials and Design
Jahrgang223.2022
AusgabenummerNovember
DOIs
PublikationsstatusVeröffentlicht - Nov. 2022
Extern publiziertJa

Bibliographische Notiz

Publisher Copyright:
© 2022

Dieses zitieren