T1 - Dual-Wavelength Vat Photopolymerization 3D Printing with Hybrid Acrylate-Epoxy Resins
T2 - Influence of Resin Composition on Microstructure and Mechanical Properties
AU - Cazin, Ines
AU - Plevová, Kateřina
AU - Alabiso, Walter
AU - Vidović, Elvira
AU - Schlögl, Sandra
N1 - Publisher Copyright: © 2024 Wiley-VCH GmbH.
PY - 2024/4
Y1 - 2024/4
N2 - Dual-wavelength vat photopolymerization 3D printing represents a convenient technology for the fabrication of objects with heterogeneous and locally controlled mechanical properties. By using two λ-orthogonal cross-linking reactions, it is possible to produce soft and stiff photopolymers with a single resin vat by switching the light source. Herein, hybrid acrylate-epoxy resins are selectively cured by using either visible or UV light. At 405 nm, a free radical curing of the acrylate monomers is induced while irradiation with 365 nm triggers an additional cationic ring opening reaction of the epoxy monomer yielding interpenetrating photopolymer networks. In a comprehensive approach, the influence of the resin composition and the applied wavelength on cure kinetics, film morphology, (thermo)mechanical properties, and printability are studied. Fully separated as well as homogenous network morphologies are obtained depending on the ratio between acrylate and epoxy monomers, cure rate and applied light source (405 vs 365 nm). In general, glass transition temperature, stiffness, and tensile strength of the photopolymers increase with rising epoxy content. In contrast, a higher epoxy concentration in combination with a higher amount of the cationic photoinitiator compromises on the system's orthogonality, giving rise to the important role of the resin composition in dual-wavelength vat photopolymerization 3D printing.
AB - Dual-wavelength vat photopolymerization 3D printing represents a convenient technology for the fabrication of objects with heterogeneous and locally controlled mechanical properties. By using two λ-orthogonal cross-linking reactions, it is possible to produce soft and stiff photopolymers with a single resin vat by switching the light source. Herein, hybrid acrylate-epoxy resins are selectively cured by using either visible or UV light. At 405 nm, a free radical curing of the acrylate monomers is induced while irradiation with 365 nm triggers an additional cationic ring opening reaction of the epoxy monomer yielding interpenetrating photopolymer networks. In a comprehensive approach, the influence of the resin composition and the applied wavelength on cure kinetics, film morphology, (thermo)mechanical properties, and printability are studied. Fully separated as well as homogenous network morphologies are obtained depending on the ratio between acrylate and epoxy monomers, cure rate and applied light source (405 vs 365 nm). In general, glass transition temperature, stiffness, and tensile strength of the photopolymers increase with rising epoxy content. In contrast, a higher epoxy concentration in combination with a higher amount of the cationic photoinitiator compromises on the system's orthogonality, giving rise to the important role of the resin composition in dual-wavelength vat photopolymerization 3D printing.
KW - dual-wavelength vat photopolymerization 3D printings
KW - heterogeneous properties
KW - hybrid radical/cationic photopolymers
KW - multi-materials
KW - polymer morphologies
UR - http://www.scopus.com/inward/record.url?scp=85187500695&partnerID=8YFLogxK
U2 - 10.1002/adem.202301699
DO - 10.1002/adem.202301699
M3 - Article
AN - SCOPUS:85187500695
SN - 1438-1656
VL - 26.2024
JO - Advanced Engineering Materials
JF - Advanced Engineering Materials
IS - 8
M1 - 2301699
ER -