Abstract
Perovskite-type oxides are highly flexible materials that show properties that are beneficial for application in reverse water-gas shift processes (rWGS). Due to their stable nature, the ability to incorporate catalytically active dopants in their lattice structure, and the corresponding feature of nanoparticle exsolution, they are promising candidates for a materials design approach. On an industrial level, the rWGS has proven to be an excellent choice for the efficient utilisation of CO2 as an abundant and renewable carbon source, reflected by the current research on novel and improved catalyst materials. In the current study, a correlation between rWGS reaction environments (CO2 to H2 ratios and temperature), surface morphology, and catalytic activity of three perovskite catalysts (Nd0.6Ca0.4Fe0.9Co0.1O3-δ, Nd0.6Ca0.4Fe0.97Co0.03O3-δ, and Nd0.6Ca0.4Fe0.97Ni0.03O3-δ) is investigated, combining catalytic measurements with SEM and NAP-XPS. The materials were found to react dynamically to the conditions showing both activation due to in situ nanoparticle exsolution and deactivation via CaCO3 formation. This phenomenon could be influenced by choice of material and conditions: less reductive conditions (larger CO2 to H2 or lower temperature) lead to smaller exsolved particles and reduced carbonate formation. However, the B-site doping was also important; only with 10% Co-doping, a predominant activation could be achieved.
Originalsprache | Englisch |
---|---|
Aufsatznummer | 1484 |
Seitenumfang | 21 |
Fachzeitschrift | Catalysts |
Jahrgang | 11.2021 |
Ausgabenummer | 12 |
DOIs | |
Publikationsstatus | Veröffentlicht - 3 Dez. 2021 |
Extern publiziert | Ja |
Bibliographische Notiz
Funding Information:Funding: This project has received funding from the European Research Council (ERC) under the European Union′s Horizon 2020 research and innovation programme (grant agreement n° 755744/ERC—Starting Grant TUCAS).
Funding Information:
This project has received funding from the European Research Council (ERC) under the European Union?s Horizon 2020 research and innovation programme (grant agreement n? 755744/ERC?Starting Grant TUCAS).
Publisher Copyright:
© 2021 by the authors. Licensee MDPI, Basel, Switzerland.