Utilization of Renewable Carbon in Electric Arc Furnace-Based Steel Production: Comparative Evaluation of Properties of Conventional and Non-Conventional Carbon-Bearing Sources

Lina Kieush, Johannes Schenk, Andrii Koveria, Gerd Rantitsch, Andrii Hrubiak, Horst Hopfinger

Publikation: Beitrag in FachzeitschriftArtikelForschungBegutachtung

4 Zitate (Scopus)

Abstract

Conventional (anthracite, calcined petroleum coke, and coke) and non-conventional (biochar, and biocokes (3 wt.% torrefied wood, and 3 wt.% petroleum coke + 3 wt.% charcoal)) carbon-bearing sources have been studied for their use in electric arc furnace (EAF)-based steel production. Commonly, for the use of carbon sources in EAFs, one of the important properties is the content of fixed carbon, the release of volatiles as well as the elemental composition of inorganics. The properties of six carbon sources were analyzed by determining the proximate analysis, X-ray fluorescence analysis (XRF), coke reactivity index (CRI), and strength after reaction with CO2 (CSR), Brunauer–Emmett–Teller (BET) specific surface area and Barrett–Joyner–Halenda (BJH) pore size and volume analysis, ash chemical analysis, optical and scanning microscopy, Raman spectroscopy and X-ray diffraction (XRD) analysis. The results indicate biocoke as a promising option to replace conventional carbon-bearing sources. In the sample set, the fixed carbon, volatiles, and ash content of the biocokes were similar despite the total difference in additives. Additionally, the use of additives did not significantly affect the biocoke reactivity indices, but slightly decreased the strength after the reaction with CO2. Carbon-bearing sources have been characterized in terms of their structural properties. XRD analysis revealed that the amount of disordered carbon increased in the order: coke < calcined petroleum coke ~ biocoke (3 wt.% torrefied wood) < biocoke (3 wt.% petroleum coke + 3 wt.% charcoal) < biochar. The results obtained on the physical, chemical, and structural properties of carbon sources are the basis for further research on the behavior of slag foaming.
OriginalspracheEnglisch
Aufsatznummer722
Seitenumfang16
FachzeitschriftMetals
Jahrgang13.2023
Ausgabenummer4
DOIs
PublikationsstatusVeröffentlicht - 6 Apr. 2023

Bibliographische Notiz

Publisher Copyright:
© 2023 by the authors.

Dieses zitieren