A tailored TiAl alloy for the powder bed based laser additive manufacturing

David Schimbäck

Research output: ThesisMaster's Thesis

220 Downloads (Pure)

Abstract

Modern combustion-based propulsion systems for automotive use and aerospace jet engines rely on innovative high-temperature lightweight materials and advanced manufacturing processes. Due to their high melting point and low density, alloys based on intermetallic titanium aluminides have a particularly high potential, which is already being used industrially. Through the development of powder-based additive manufacturing processes, conditions have been created in recent years representing a paradigm shift for the future production of components as well as their properties and design. For this purpose, samples of an intermetallic γ-titanium aluminide alloy, the so-called TNM alloy, were produced via a powder-bed-based selective laser melting (SLM) and subjected to extensive metallurgical characterization by means of light and scanning electron microscopy, electron probe microanalysis, differential scanning calorimetry and X-ray diffraction. In order to avoid a micro notch effect due to increased porosity, which has a negative effect on fatigue and (fracture) toughness properties in the case of high-strength materials, a hot-isostatic pressing was carried out as the first heat treatment step. Subsequently, a heat treatment was performed to adjust a microstructure with balanced properties for the use at high temperatures to ensure a sufficient elongation at break and fracture toughness at room temperature. The aim of the microstructural investigations was to characterize the initial state of the powder, to record occurring porosity, to investigate chemical anisotropies and to adapt the microstructure for high-temperature applications. By means of the results of the applied methods, the density of the as-SLM material could be increased to 99.9% and a suitable heat treatment for the present alloy was developed which includes a homogeneous nearly lamellar microstructure with globular γ-phase (NLγ) as well as a fully lamellar microstructure (FL). Furthermore, the mechanical properties of the material were investigated by creep tests and three-point bending tests.
Translated title of the contributionEine maßgeschneiderte TiAl-Legierung für die pulverbettbasierte laseradditive Fertigung
Original languageEnglish
QualificationDipl.-Ing.
Awarding Institution
  • Montanuniversität
Supervisors/Advisors
  • Mayer, Svea, Supervisor (internal)
  • Leichtfried, Gerhard, Co-Supervisor (external), External person
Award date12 Apr 2019
Publication statusPublished - 2019

Bibliographical note

embargoed until 02-04-2020

Keywords

  • selective laser melting
  • additive manufacturing
  • titanium aluminides
  • microstructure
  • creep testing