T1 - Experimental Study of High Temperature Phase Equilibria in the Iron-Rich Part of the Fe-P and Fe-C-P Systems
AU - Bernhard, Michael Christian
AU - Presoly, Peter
AU - Fuchs, Nora
AU - Bernhard, Christian
AU - Kang, Youn-Bae
PY - 2020/7/23
Y1 - 2020/7/23
N2 - During the solidification of steel, phosphorus strongly segregates in the interdendritic liquid phase. In the continuous casting process, even low levels of P may have a detrimental effect on the final product quality. However, phosphorus is partly added up to 0.10 wt pct to improve the mechanical properties of advanced steel grades nowadays, e.g., High-Strength Interstitial-Free (HSIF). To provide new experimental data for the development of thermodynamic databases and solidification models for P alloyed steel grades, phase equilibria in the Fe-P and Fe-C-P key systems were studied up to 1550 °C using differential scanning calorimetry (DSC) and high temperature laser scanning confocal microscopy (HT-LSCM). Special focus was placed on solid/liquid equilibrium temperatures in the Fe-rich part of the binary Fe-P system between 0.025 and 9 wt pct P. In the ternary system, three isoplethal sections with 0.10 mass pct. P, 0.20 mass pct. C and constant mass percent ratio P/C of 2 were investigated. In the latter section, HT-LSCM observations were linked with DSC signals to optically identify present phase stabilities. Particularly at [pct P] < 1, significant differences between performed measurements and calculated phase equilibrium temperatures using thermodynamic assessments from the literature were identified. In all ternary sections, the experiments indicate less influence of P on the hypo-peritectic range compared to the thermodynamic calculations.
AB - During the solidification of steel, phosphorus strongly segregates in the interdendritic liquid phase. In the continuous casting process, even low levels of P may have a detrimental effect on the final product quality. However, phosphorus is partly added up to 0.10 wt pct to improve the mechanical properties of advanced steel grades nowadays, e.g., High-Strength Interstitial-Free (HSIF). To provide new experimental data for the development of thermodynamic databases and solidification models for P alloyed steel grades, phase equilibria in the Fe-P and Fe-C-P key systems were studied up to 1550 °C using differential scanning calorimetry (DSC) and high temperature laser scanning confocal microscopy (HT-LSCM). Special focus was placed on solid/liquid equilibrium temperatures in the Fe-rich part of the binary Fe-P system between 0.025 and 9 wt pct P. In the ternary system, three isoplethal sections with 0.10 mass pct. P, 0.20 mass pct. C and constant mass percent ratio P/C of 2 were investigated. In the latter section, HT-LSCM observations were linked with DSC signals to optically identify present phase stabilities. Particularly at [pct P] < 1, significant differences between performed measurements and calculated phase equilibrium temperatures using thermodynamic assessments from the literature were identified. In all ternary sections, the experiments indicate less influence of P on the hypo-peritectic range compared to the thermodynamic calculations.
UR - http://www.scopus.com/inward/record.url?scp=85086630973&partnerID=8YFLogxK
U2 - 10.1007/s11661-020-05912-z
DO - 10.1007/s11661-020-05912-z
M3 - Article
SN - 1073-5623
VL - 51.2020
SP - 5351
EP - 5364
JO - Metallurgical and materials transactions. A, Physical metallurgy and materials science
JF - Metallurgical and materials transactions. A, Physical metallurgy and materials science
IS - 10
ER -