Influence of multilayer architecture on microstructure and fracture properties of arc evaporated TiAlTaN coatings

Helene Waldl, Michael Tkadletz, Christoph Czettl, Markus Pohler, Nina Schalk

Research output: Contribution to journalArticleResearchpeer-review


The incorporation of a fourth element in Ti 1-xAl xN, like Ta, and a multilayer architecture are possible concepts to further enhance the coating performance in cutting applications. In the present study, both concepts are combined, focusing on the investigation of the microstructure and the fracture properties of two Ti 1-x-yAl xTa yN single layer coatings (Ti 0.55Al 0.44Ta 0.01N and Ti 0.33Al 0.54Ta 0.13N) and two corresponding multilayer coatings with the same bilayer thickness but an inverse layer sequence with different layer thicknesses. Energy dispersive X-Ray spectroscopy was utilized to determine the average composition of the coatings, confirming that the Al and Ta contents increase from single layer Ti 0.55Al 0.44Ta 0.01N via the two multilayers to single layer Ti 0.33Al 0.5 4Ta 0.1 3N. The residual stress and microstructure were studied using X-ray diffraction and scanning electron microscopy revealing higher compressive stress and grain refinement with higher Al and Ta content, which provoked an increasing hardness as evidenced by nanoindentation experiments. In contrast, the contribution of the multilayer architecture to the hardness increase is only minor. Additionally, micromechanical bending tests revealed a trend of higher fracture stress with increasing Al and Ta content. The fracture toughness was constant for all coatings as different toughening mechanisms occur.

Original languageEnglish
Article number128098
Number of pages7
JournalSurface & coatings technology
Issue number15 March
Early online date10 Jan 2022
Publication statusPublished - 15 Mar 2022

Bibliographical note

Publisher Copyright: © 2022 The Author(s)

Cite this