TY - JOUR
T1 - Recovery of Molybdenum, Chromium, Tungsten, Copper, Silver, and Zinc from Industrial Waste Waters Using Zero-Valent Iron and Tailored Beneficiation Processes
AU - Vollprecht, Daniel
AU - Plessl, Katharina
AU - Neuhold, Simone Franziska
AU - Kittinger, Friedrich
AU - Öfner, Wolfgang
AU - Müller, Peter
AU - Mischitz, Robert
AU - Sedlazeck, Klaus Philipp
N1 - Publisher Copyright: © 2020 by the authors.
PY - 2020/2/28
Y1 - 2020/2/28
N2 - Zero-valent iron (ZVI) has been used for water treatment for more than 160 years. However, passivation of its surface often constituted a problem which could only be tackled recently by the innovative Ferrodecont process using a fluidized bed reactor. In this study, pilot scale experiments for the removal of Mo, Cr, W, Cu, Ag and Zn from two industrial waste water samples and lab-scale experiments for the beneficiation of the abrasion products are presented to integrate the Ferrodecont process into a complete recycling process chain. Firstly, 38.5 % of Cu was removed from sample A, yielding abrasion products containing 33.1 wt% Cu as metallic copper (Cu) and various Cu compounds. The treatment of sample B removed 99.8 % of Mo, yielding abrasion products containing 17.8 wt% of Mo as amorphous phases or adsorbed species. Thermal treatment (1300 °C) of the abrasion product A indicated a reduction of delafossite to metallic Cu according to differential scanning calorimetry (DSC), thermogravimetry (TG) and X-ray diffraction (XRD), which was successfully separated from the magnetic iron phases. Hydrometallurgical treatment (1.5 M NaOH, 3 d, liquid:solid ratio (L:S) = 15:1) of sample B yielded aqueous extracts with Mo concentrations of 5820 to 6300 mgL-1. In conclusion, this corresponds to an up to 53-fold enrichment of Mo during the entire process chain.
AB - Zero-valent iron (ZVI) has been used for water treatment for more than 160 years. However, passivation of its surface often constituted a problem which could only be tackled recently by the innovative Ferrodecont process using a fluidized bed reactor. In this study, pilot scale experiments for the removal of Mo, Cr, W, Cu, Ag and Zn from two industrial waste water samples and lab-scale experiments for the beneficiation of the abrasion products are presented to integrate the Ferrodecont process into a complete recycling process chain. Firstly, 38.5 % of Cu was removed from sample A, yielding abrasion products containing 33.1 wt% Cu as metallic copper (Cu) and various Cu compounds. The treatment of sample B removed 99.8 % of Mo, yielding abrasion products containing 17.8 wt% of Mo as amorphous phases or adsorbed species. Thermal treatment (1300 °C) of the abrasion product A indicated a reduction of delafossite to metallic Cu according to differential scanning calorimetry (DSC), thermogravimetry (TG) and X-ray diffraction (XRD), which was successfully separated from the magnetic iron phases. Hydrometallurgical treatment (1.5 M NaOH, 3 d, liquid:solid ratio (L:S) = 15:1) of sample B yielded aqueous extracts with Mo concentrations of 5820 to 6300 mgL-1. In conclusion, this corresponds to an up to 53-fold enrichment of Mo during the entire process chain.
UR - http://www.scopus.com/inward/record.url?scp=85081984942&partnerID=8YFLogxK
U2 - 10.3390/pr8030279
DO - 10.3390/pr8030279
M3 - Article
SN - 2227-9717
VL - 8.2020
JO - Processes : open access journal
JF - Processes : open access journal
IS - 3
M1 - 279
ER -