Influence of Different Carbon Content on Reduction of Zinc Oxide via Metal Bath

Publikationen: Beitrag in FachzeitschriftArtikelForschung(peer-reviewed)

Standard

Influence of Different Carbon Content on Reduction of Zinc Oxide via Metal Bath. / Auer, Michael; Antrekowitsch, Jürgen; Wölfler, Christoph.

in: Applied Sciences, Jahrgang 12.2022, Nr. 2, 12020664, 11.01.2022.

Publikationen: Beitrag in FachzeitschriftArtikelForschung(peer-reviewed)

Bibtex - Download

@article{e071bc534a604d289ef6fc477722326d,
title = "Influence of Different Carbon Content on Reduction of Zinc Oxide via Metal Bath",
abstract = "Electric arc furnace dust (EAFD) is an important secondary resource for the zinc industry. The most common process for its recycling is the pyro-metallurgical treatment in the Waelz process. However, this process focuses on the recycling of the zinc, whereas the recovery of other metals from the EAFD—such as iron and other alloying elements—is neglected. An up-to-date version of reprocessing can involve multi-metal recycling by means of a metal bath containing carbon. The use of a liquid iron alloy requires a higher processing temperature, which enables the reduction and melting of iron oxides as well as other compounds occurring in the dust. Furthermore, the Zn yield is higher and the reduction kinetics are faster than in the Waelz process. This paper is only focused on the zinc reduction in such a metal bath. In order to determine the influence of the carbon content in the molten metal on the reduction rate, experiments were carried out on the reduction behavior of zinc oxide using a synthetic slag. This slag, with a basicity B2 = 1, was applied to an iron bath with varying carbon contents. (0.85%, 2.16%, 2.89%, and 4.15%) The decrease in the zinc oxide concentration was monitored, along with the reaction rates calculated from these data. It was found that the reaction rate increases with rising carbon content in the melt.",
author = "Michael Auer and J{\"u}rgen Antrekowitsch and Christoph W{\"o}lfler",
year = "2022",
month = jan,
day = "11",
doi = "10.3390/app12020664",
language = "English",
volume = "12.2022",
journal = " Applied Sciences",
issn = "2076-3417",
publisher = "Multidisciplinary Digital Publishing Institute (MDPI)",
number = "2",

}

RIS (suitable for import to EndNote) - Download

TY - JOUR

T1 - Influence of Different Carbon Content on Reduction of Zinc Oxide via Metal Bath

AU - Auer, Michael

AU - Antrekowitsch, Jürgen

AU - Wölfler, Christoph

PY - 2022/1/11

Y1 - 2022/1/11

N2 - Electric arc furnace dust (EAFD) is an important secondary resource for the zinc industry. The most common process for its recycling is the pyro-metallurgical treatment in the Waelz process. However, this process focuses on the recycling of the zinc, whereas the recovery of other metals from the EAFD—such as iron and other alloying elements—is neglected. An up-to-date version of reprocessing can involve multi-metal recycling by means of a metal bath containing carbon. The use of a liquid iron alloy requires a higher processing temperature, which enables the reduction and melting of iron oxides as well as other compounds occurring in the dust. Furthermore, the Zn yield is higher and the reduction kinetics are faster than in the Waelz process. This paper is only focused on the zinc reduction in such a metal bath. In order to determine the influence of the carbon content in the molten metal on the reduction rate, experiments were carried out on the reduction behavior of zinc oxide using a synthetic slag. This slag, with a basicity B2 = 1, was applied to an iron bath with varying carbon contents. (0.85%, 2.16%, 2.89%, and 4.15%) The decrease in the zinc oxide concentration was monitored, along with the reaction rates calculated from these data. It was found that the reaction rate increases with rising carbon content in the melt.

AB - Electric arc furnace dust (EAFD) is an important secondary resource for the zinc industry. The most common process for its recycling is the pyro-metallurgical treatment in the Waelz process. However, this process focuses on the recycling of the zinc, whereas the recovery of other metals from the EAFD—such as iron and other alloying elements—is neglected. An up-to-date version of reprocessing can involve multi-metal recycling by means of a metal bath containing carbon. The use of a liquid iron alloy requires a higher processing temperature, which enables the reduction and melting of iron oxides as well as other compounds occurring in the dust. Furthermore, the Zn yield is higher and the reduction kinetics are faster than in the Waelz process. This paper is only focused on the zinc reduction in such a metal bath. In order to determine the influence of the carbon content in the molten metal on the reduction rate, experiments were carried out on the reduction behavior of zinc oxide using a synthetic slag. This slag, with a basicity B2 = 1, was applied to an iron bath with varying carbon contents. (0.85%, 2.16%, 2.89%, and 4.15%) The decrease in the zinc oxide concentration was monitored, along with the reaction rates calculated from these data. It was found that the reaction rate increases with rising carbon content in the melt.