Influence of Hatch Strategy on Crystallographic Texture Evolution, Mechanical Anisotropy of Laserbeam Powder Bed Fused S316L Steel

Publikationen: Beitrag in FachzeitschriftArtikelForschung(peer-reviewed)

Externe Organisationseinheiten

  • Resch GmbH, Glojach
  • Helmholtz-Zentrum Hereon, Geesthacht
  • Erich Schmid Institute of Materials Science of the Austrian Academy of Sciences, Leoben

Abstract

The correlations between process conditions, microstructure and mechanical properties of additively manufactured components are not fully understood yet. In this contribution, three different hatch strategies are used to fabricate rod-like samples from S316L stainless steel, which are further investigated using synchrotron diffraction, optical microscopy and tensile tests. The results indicate the presence of ⟨110⟩ biaxial and fiber textures, whose sharpness depends on the applied hatch strategy. Mechanical tests reveal a strong correlation of the samples’ response to the observed anisotropy in the plane perpendicular to the build direction. Even though the average yield and ultimate tensile strengths of around 475 and 500 MPa, respectively, do not differ significantly, the stress-strain behavior can be correlated to the observed in-plane anisotropy. Particularly, twinning induced plasticity, a distinct increase of the work hardening rate at larger strains and elliptical necking are observed in some samples with biaxial (Goss) texture. These findings indicate that texture design by means of applying dedicated hatch strategies can be used to effectively tune the multiaxial deformation behavior of components produced by laser powder bed fusion.

Details

OriginalspracheEnglisch
Seitenumfang25
FachzeitschriftAdvanced engineering materials
Jahrgang2022
Ausgabenummer??? Stand: 13. October
DOIs
StatusVeröffentlicht - 2 Aug 2022