Microstructural evolution and thermal stability of AlCr(Si)N hard coatings revealed by in-situ high-temperature high-energy grazing incidence transmission X-ray diffraction

Publikationen: Beitrag in FachzeitschriftArtikelForschung(peer-reviewed)

Standard

Microstructural evolution and thermal stability of AlCr(Si)N hard coatings revealed by in-situ high-temperature high-energy grazing incidence transmission X-ray diffraction. / Jäger, Nikolaus; Meindlhumer, Michael; Spor, S.; Hruby, Hynek; Julin, J. ; Stark, Andreas; Nahif, F.; Keckes, Julius; Mitterer, Christian; Daniel, Rostislav.

in: Acta materialia, Jahrgang 186.2020, Nr. March, 18.01.2020, S. 545-554.

Publikationen: Beitrag in FachzeitschriftArtikelForschung(peer-reviewed)

Bibtex - Download

@article{a011f85d9904415da51a35d7de54497d,
title = "Microstructural evolution and thermal stability of AlCr(Si)N hard coatings revealed by in-situ high-temperature high-energy grazing incidence transmission X-ray diffraction",
abstract = "An extensive understanding about the microstructural evolution and thermal stability of the metastable AlCr(Si)N coating system is of considerable importance for applications facing high temperatures, but it is also a challenging task since several superimposed processes simultaneously occur at elevated temperatures. In this work, three AlCr(Si)N coatings with 0 at%., 2.5 at% and 5 at% Si were investigated by in-situ high-temperature high-energy grazing incidence transmission X-ray diffraction (HT-HE-GIT-XRD) and complementary differential scanning calorimetry and thermogravimetric analysis measurements combined with conventional ex-situ X-ray diffraction. The results revealed (i) a change in the microstructure from columnar to a fine-grained nano-composite, (ii) a reduced decomposition rate of CrN to Cr 2N, also shifted to higher onset temperatures from ~ 1000 ∘C to above ~ 1100 ∘C and (iii) an increase of lattice defects and micro strains resulting in a significant increase of compressive residual strain with increasing Si content. While the Si-containing coatings in the as-deposited state show a lower hardness of 28 GPa compared to AlCrN with 32 GPa, vacuum annealing at ~ 1100 ∘C led to an increase in hardness to 29 GPa for the coatings containing Si and a decrease in hardness to 26 GPa for AlCrN. Furthermore, the in-situ HT-HE-GIT-XRD method allowed for simultaneously accessing temperature-dependent variations of the coating microstructure (defect density, grain size), residual strain state and phase stability up to ~ 1100 ∘C. Finally, the results established a deeper understanding about the relationships between the elemental composition of the materials, the resulting microstructure including crystallographic phases and residual strain state, and the coating properties from room temperature up to ~ 1100 ∘C. ",
author = "Nikolaus J{\"a}ger and Michael Meindlhumer and S. Spor and Hynek Hruby and J. Julin and Andreas Stark and F. Nahif and Julius Keckes and Christian Mitterer and Rostislav Daniel",
year = "2020",
month = jan,
day = "18",
doi = "10.1016/j.actamat.2020.01.026",
language = "English",
volume = "186.2020",
pages = "545--554",
journal = "Acta materialia",
issn = "1359-6454",
publisher = "Elsevier BV",
number = "March",

}

RIS (suitable for import to EndNote) - Download

TY - JOUR

T1 - Microstructural evolution and thermal stability of AlCr(Si)N hard coatings revealed by in-situ high-temperature high-energy grazing incidence transmission X-ray diffraction

AU - Jäger, Nikolaus

AU - Meindlhumer, Michael

AU - Spor, S.

AU - Hruby, Hynek

AU - Julin, J.

AU - Stark, Andreas

AU - Nahif, F.

AU - Keckes, Julius

AU - Mitterer, Christian

AU - Daniel, Rostislav

PY - 2020/1/18

Y1 - 2020/1/18

N2 - An extensive understanding about the microstructural evolution and thermal stability of the metastable AlCr(Si)N coating system is of considerable importance for applications facing high temperatures, but it is also a challenging task since several superimposed processes simultaneously occur at elevated temperatures. In this work, three AlCr(Si)N coatings with 0 at%., 2.5 at% and 5 at% Si were investigated by in-situ high-temperature high-energy grazing incidence transmission X-ray diffraction (HT-HE-GIT-XRD) and complementary differential scanning calorimetry and thermogravimetric analysis measurements combined with conventional ex-situ X-ray diffraction. The results revealed (i) a change in the microstructure from columnar to a fine-grained nano-composite, (ii) a reduced decomposition rate of CrN to Cr 2N, also shifted to higher onset temperatures from ~ 1000 ∘C to above ~ 1100 ∘C and (iii) an increase of lattice defects and micro strains resulting in a significant increase of compressive residual strain with increasing Si content. While the Si-containing coatings in the as-deposited state show a lower hardness of 28 GPa compared to AlCrN with 32 GPa, vacuum annealing at ~ 1100 ∘C led to an increase in hardness to 29 GPa for the coatings containing Si and a decrease in hardness to 26 GPa for AlCrN. Furthermore, the in-situ HT-HE-GIT-XRD method allowed for simultaneously accessing temperature-dependent variations of the coating microstructure (defect density, grain size), residual strain state and phase stability up to ~ 1100 ∘C. Finally, the results established a deeper understanding about the relationships between the elemental composition of the materials, the resulting microstructure including crystallographic phases and residual strain state, and the coating properties from room temperature up to ~ 1100 ∘C.

AB - An extensive understanding about the microstructural evolution and thermal stability of the metastable AlCr(Si)N coating system is of considerable importance for applications facing high temperatures, but it is also a challenging task since several superimposed processes simultaneously occur at elevated temperatures. In this work, three AlCr(Si)N coatings with 0 at%., 2.5 at% and 5 at% Si were investigated by in-situ high-temperature high-energy grazing incidence transmission X-ray diffraction (HT-HE-GIT-XRD) and complementary differential scanning calorimetry and thermogravimetric analysis measurements combined with conventional ex-situ X-ray diffraction. The results revealed (i) a change in the microstructure from columnar to a fine-grained nano-composite, (ii) a reduced decomposition rate of CrN to Cr 2N, also shifted to higher onset temperatures from ~ 1000 ∘C to above ~ 1100 ∘C and (iii) an increase of lattice defects and micro strains resulting in a significant increase of compressive residual strain with increasing Si content. While the Si-containing coatings in the as-deposited state show a lower hardness of 28 GPa compared to AlCrN with 32 GPa, vacuum annealing at ~ 1100 ∘C led to an increase in hardness to 29 GPa for the coatings containing Si and a decrease in hardness to 26 GPa for AlCrN. Furthermore, the in-situ HT-HE-GIT-XRD method allowed for simultaneously accessing temperature-dependent variations of the coating microstructure (defect density, grain size), residual strain state and phase stability up to ~ 1100 ∘C. Finally, the results established a deeper understanding about the relationships between the elemental composition of the materials, the resulting microstructure including crystallographic phases and residual strain state, and the coating properties from room temperature up to ~ 1100 ∘C.

UR - http://www.scopus.com/inward/record.url?scp=85078436825&partnerID=8YFLogxK

U2 - 10.1016/j.actamat.2020.01.026

DO - 10.1016/j.actamat.2020.01.026

M3 - Article

VL - 186.2020

SP - 545

EP - 554

JO - Acta materialia

JF - Acta materialia

SN - 1359-6454

IS - March

ER -