MICROSTRUCTURAL EVOLUTION OF BLAST FURNACE COKE DURING EXPERIMENTAL HEATING – THE IFORS APPROACH

Publikationen: Beitrag in Buch/Bericht/KonferenzbandBeitrag in KonferenzbandForschung

Abstract

Furnace coke was experimental heated between 850°C and 1100°C by varying the gas composition and the alkali content of the raw coke. Raman spectroscopy (Iterative Fitting of Raman Spectra) evaluates the microstructural change of coke during the experiments. The obtained results indicate a significant microstructural variation within a bulk sample. This variation controls significantly the coke quality as estimated from standard experiments (CRI 23.9 - 38.3). A bulk sample with a CRI value <30 is composed dominantly of lumps showing a relatively low structural ordering. During experimental heating, the structural ordering of such lumps increases. A bulk sample with a CRI value >30 is composed dominantly of lumps showing a relatively high structural ordering. During experimental heating, the structural state of such lumps remains unchanged unless a strong reaction is induced by adding alkaline elements. It is suggested that under laboratory conditions, thermal and chemical energy, affecting a microstructurally low-ordered coke, first reorganizes the structural state of the individual coke lumps, retarding the onset of the Boudouard Reaction.

Details

OriginalspracheEnglisch
TitelProceedings of 8th International Congress on Science and Technology of Ironmaking
StatusVeröffentlicht - Sep 2018
Veranstaltung8th ICSTI - Vienna, Österreich
Dauer: 25 Sep 201828 Sep 2018

Konferenz

Konferenz8th ICSTI
LandÖsterreich
OrtVienna
Zeitraum25/09/1828/09/18