On the Transferability of Fatigue and Cyclic Deformation Data to 100 µm Thin Structures

Publikationen: Beitrag in FachzeitschriftArtikelForschung(peer-reviewed)

Externe Organisationseinheiten

  • LEC GmbH


The fatigue properties and cyclic deformation behaviour of materials are usually determined using cylindrical specimens (e.g., Ø7.5 mm). Since the transferability to very small dimensions has not been comprehensively considered so far, this study investigates the transferability of specimen data from high-strength steel X5CrNiCuNb16-4 to real structures characterised by a wall thickness of 100 µm. Regarding fatigue, extensive calculations demonstrate that for notched specimens and thin structures, both the material-mechanical support factor concept according to the FKM guideline and the point method of the Theory of Critical Distance (TCD) make correct predictions of the local fatigue strength, with a maximum deviation from experimental values of less than 5%. However, the study points out that the TCD is only conditionally applicable for thin-walled structures, as the material parameter a0 must be significantly smaller than the wall thickness. Regarding the deformation behaviour, the material reveals special flow characteristics in the first hysteresis. Nevertheless, a combined hardening approach is suitable for modelling. The validation of the model by a plastic deformation of the structure seems plausible, although geometric influences prove to be dominant. In conclusion, even 100 µm thin structures can be evaluated using conventional specimen tests and established assessment or modelling methods.


StatusVeröffentlicht - 15 Sep. 2022