Microstructure and mechanical properties of arc evaporated Ti(Al,Si)N coatings

Research output: Contribution to journalArticleResearchpeer-review

External Organisational units

  • Ceratizit Austria GmbH
  • Christian Doppler Laboratory of Advanced Coated Cutting Tools

Abstract

Ti(Al)SiN protective hard coatings are promising candidates for the metal cutting industry, due to their favorable properties such as a high hardness and good oxidation resistance. Within the scope of this work, the microstructure of cathodic arc evaporated TiN, Ti 84Si 16N, Ti 81Al 3Si 16N and Ti 70Al 14Si 16N was correlated with their mechanical properties. X-ray diffraction (XRD) as well as scanning electron microscopy investigations of the cross-sections revealed a pronounced grain refinement for Ti(Al)SiN compared to TiN. The texture of the coatings was analyzed by XRD pole-figures, showing a change in the preferred orientation in growth direction from (111) for TiN to (200) for Ti(Al)SiN. Hardness values were found to strongly increase from 29 GPa to 40 GPa upon Si addition, but remained constant for further alloying with Al. Micromechanical bending tests allowed to gain a detailed insight into the fracture properties of the investigated coatings and revealed an enhanced fracture stress and fracture toughness (K IC) for Ti(Al)SiN compared to TiN. Hereby, the K IC value of 2.4 ± 0.3 MPa m 1/2 for TiN could be increased to a maximum of 3.3 ± 0.2 MPa m 1/2 for Ti 70Al 14Si 16N. The present findings provide a systematic overview of the microstructure and mechanical properties of arc evaporated Ti(Al,Si)N coatings, thus allowing to select the most suitable coatings for different applications in the cutting industry.

Details

Original languageEnglish
Article number127461
Number of pages8
JournalSurface & coatings technology
Volume421.2021
Issue number15 September
Early online date26 Jun 2021
DOIs
Publication statusPublished - 15 Sep 2021