Precipitation reactions in a Cu-Ni-Al medium carbon alloyed dual hardening steel

Research output: Contribution to journalReview articleResearchpeer-review

Authors

Organisational units

External Organisational units

  • voestalpine BÖHLER Edelstahl GmbH & Co KG

Abstract

Dual hardening steels achieve secondary hardening through the combined precipitation of intermetallic phases and carbides. The early stages of precipitation of a Cu-Ni-Al medium carbon alloyed dual hardening steel with a low alloying ratio of Cu/NiAl were investigated. Phase separation during continuous heating with 20 K min 1 was identified to occur in the temperature range from 360 °C to 620 °C by differential scanning calorimetry. The precipitates were characterized utilizing atom probe tomography. Different cluster search algorithms were used in order to determine the sequence of phase separation and thus identify the individual precipitation reactions. It was shown that phase separation starts with the formation of Cu (Ni, Al, Mn) clusters. At an ageing temperature of 580 °C, heterogeneous precipitation of VC-clusters at the interfaces between the Cu-precipitates and the iron matrix takes place. A phase separation of the Cu (Ni, Al, Mn) clusters into separate Cu and NiAl particles could not be observed up to an ageing temperature of 620 °C. The sequence of precipitation is thus determined to be Cu-VC-NiAl.

Details

Original languageEnglish
Article number110126
Number of pages9
JournalMaterials characterization
Volume160.2020
Issue numberFebruary
DOIs
Publication statusE-pub ahead of print - 9 Jan 2020